Increasing Compressive Strength of Self Compacting Concrete with MasterGlenium and MasterSure
DOI:
https://doi.org/10.30737/ukarst.v8i1.5565Keywords:
Compressive Strength, Concrete, MasterGlenium, MasterSureAbstract
The growth in development complexity demands innovation in the construction industry. Self-compacting concrete (SCC) can flow and fill mold cavities without additional vibration, offering an efficient solution for structures with complex shapes or tight spaces. In addition, SCC can speed up bonding and simplify workability by adding MasterGlenium and MasterSure superplasticizers. However, its use is limited due to a lack of understanding of the optimal composition of the mixture. The research aims to determine the effect of adding MasterGlenium and Maste Sure in the concrete mixture on the compressive strength of concrete. Experimental research was conducted with a mixture of MasterGlenium additives at 0.25%, 0,30%, 0,35%, 0.40%, and MasterSure 0.30% of the total binder. Slump and compressive strength tests of concrete are carried out to determine workability and quality performance. The research results showed that the optimal concrete mix with the addition of MasterGlenium 0.35% and MasterSure 0.30% was 25.39 Mpa, higher than Normal concrete 15.21 Mpa. The slump test results confirm that the concrete is classified as SCC. This shows the importance of the composition of MasterGlenium and MasterSure superplasticizers on the compressive strength of SCC concrete. So, the results of this research can be used to improve the quality of concrete structure projects.
References
R. G. Satria, W. Wibowo, and E. Safitri, “Pengaruh Kadar Fly Ash Terhadap Kuat Tekan Pada High Volume Fly Ash Self Compacting Concrete (Hvfa-Scc) Benda Uji Silinder D 7,5 Cm X 15 Cm Usia 14, 28 Dan 90 Hari,” Matriks Tek. Sipil, vol. 7, no. 3, pp. 226–232, 2019, doi: 10.20961/mateksi.v7i3.36492.
A. Pujianto, R. Faizah, D. A. Wijaya, J. Abdurazak, H. Prayuda, and H. Wijaya, “Kuat Tekan dan Tarik Belah Beton Serat Menggunakan Aggregat Ringan,” Semesta Tek., vol. 24, no. 1, pp. 1–9, 2021, doi: 10.18196/st.v24i1.12084.
R. Amelia, S. Suhendra, and K. R. Amalia, “Hubungan Faktor-Faktor yang Mempengaruhi Kuat Tekan Beton,” J. Talent. Sipil, vol. 4, no. 2, p. 225, 2021, doi: 10.33087/talentasipil.v4i2.79.
S. K. Sahu, P. K. Behera, S. Panda, P. Choudhury, and L. Rout, “Jo ur na l P re of,” Tetrahedron, p. 131663, 2020.
F. Han, K. Huang, Y. Wei, J. Han, and Y. Xu, “The Mechanical Properties and Water-Reducing and Retarding Mechanism of a Xylonic Cement Admixture,” Materials (Basel)., vol. 16, no. 22, 2023, doi: 10.3390/ma16227096.
S. Kimi and A. A. Alghafari, “Pengaruh Penambahan Silica Fume Dan Glenium Sky Terhadap Kuat Tekan Beton K-400,” Bear. J. Penelit. dan Kaji. Tek. Sipil, vol. 6, no. 2, pp. 116–122, 2020, doi: 10.32502/jbearing.2834201962.
F. E. Poerwodihardjo and R. N. Sari, “Scc Menggunakan Agregat Pecahan Keramik,” vol. 23, no. 2, pp. 65–75, 2022.
S. Haniza, U. Jusi, and A. Saputra, “Analisis Karakteristik Beton Self Compacting Concrete Terhadap Penambahan Superplasticizer MasterGelenium ACE 8595,” J. Infrastruct. Civ. Eng., vol. 1, no. 1, pp. 68–76, 2021, doi: 10.35583/jice.v1i1.7.
A. R. K. Anam, Z. B. Mahardana, F. W. M. Aisyah, Y. M. A. Putri, and ..., “Pengaruh Penggunaan Zat Aditif Mastersure dan Masterglenium terhadap Workability Beton Normal,” Cived, vol. 10, no. 2, pp. 409–415, 2023.
M. Kurniawan, H. Ahmadi, F. Syarif, S. H. Dewi, and P. R. Setiawan, “Studi Eksperimental Penambahan Zat Additif Mastersure 1007 Terhadap Kuat Tekan Beton Silinder Fc ’ 30 Mahadi,” vol. 17, pp. 18–25, 2023.
Husnah and R. Almagany, “Uji Eksperimental Penggunaan Zat Additif Mastersure 1007 Terhadap Workobility Dan Waktu Ikat Beton,” Sainstek (e-Journal), vol. 9, no. 1, pp. 41–46, 2021, doi: 10.35583/js.v9i1.136.
D. Paerunan, J. Tanijaya, and O. J. Sanggaria, “Pengaruh Kelereng Sebagai Substitusi Agregat Kasar Pada Campuran Beton Mutu Normal,” Paulus Civ. Eng. J., vol. 5, no. 3, pp. 510–515, 2023, doi: 10.52722/pcej.v5i3.717.
A. Sudjatmiko and M. B. Zhuhur, “Pengaruh Kadar Lumpur Agregat Halus 5%, 7,5%, 10%, 12,5%, dan 15% Terhadap Kuat Tekan dan Kuat Tarik Belah,” Simp. Nas. RAPI XVIII-2019 FT UMS, no. 1, pp. 307–308, 2019.
S. Nicolaas and E. N. Slat, “Pemanfaatan Beton Pemadatan Mandiri (Self Compacting Concrete) Sebagai Balok Struktur Dengan Menggunakan Agregat Lokal,” J. Integr., vol. 11, no. 2, pp. 81–85, 2019, doi: 10.30871/ji.v11i2.1651.
M. A. A. HANAFI et al., “Efektivitas Pembuatan Beton Dengan Penggunaan Agregat Kasar Kedak,” J. Ris. Rekayasa Sipil, vol. 6, no. 2, p. 129, 2023, doi: 10.20961/jrrs.v6i2.71930.
R. D. Fatika et al., “Meningkatkan Kapasitas Kuat Tekan Beton dengan Kendala Kadar Lumpur Agregat Halus,” Cived, vol. 10, no. 1, p. 190, 2023, doi: 10.24036/cived.v10i1.121338.
M. Hudori, M. Tandedi, A. T. Sentanu, and M. A. Ferdinand, “Studi Pengujian Kadar Lumpur Agregat Halus Pada Pasir Di Kota Batam,” Racic Rab Constr. Res., vol. 7, no. 1, pp. 96–103, 2022, doi: 10.36341/racic.v7i1.2536.
W. Wibowo, S. Sunarmasto, and H. Rashad, “Kajian Kuat Tarik Langsung Dan Kuat Lekat Pada Beton Mutu Tinggi Memadat Mandiri Dengan Variasi Kadar Metakaolin,” Matriks Tek. Sipil, vol. 7, no. 4, pp. 458–465, 2019, doi: 10.20961/mateksi.v7i4.38486.
D. C. Feng et al., “Machine Learning-Based Compressive Strength Prediction for Concrete: An Adaptive Boosting Approach,” Constr. Build. Mater., vol. 230, p. 117000, 2020, doi: 10.1016/j.conbuildmat.2019.117000.
L. Maia, “Evaluation of the Fresh Properties of Cement Pastes: Part I—Response Models Applied to Changes in the One-Variable-at-a-Time Method,” Materials (Basel)., vol. 16, no. 11, 2023, doi: 10.3390/ma16114139.
J. A. Sainz-Aja et al., “Determination of the Optimum Amount of Superplasticizer Additive for Self-Compacting Concrete,” Appl. Sci., vol. 10, no. 9, 2020, doi: 10.3390/app10093096.
M. Yazid, R. R. Husaini, F. Ramdhani, H. Husnah, and S. F. Annisa, “Pengaruh Penambahan Masterglenium ACE 8595 Terhadap Kuat Tekan Beton,” J. Infrastruct. Civ. Eng., vol. 2, no. 2, pp. 106–113, 2022, doi: 10.35583/jice.v2i2.22.
P. Strzalkowski and U. Kazmierczak, “Wear and Fragmentation Resistance of Mineral Aggregates— a Review of Micro-Deval and Los Angeles Tests,” Materials (Basel)., vol. 14, no. 18, 2021, doi: 10.3390/ma14185456.
S. Bhavanishankar, “Study on Rheological & Mechanical Properties of SCM using Mineral Admixture as a Partial Replacement of Cement,” Int. Res. J. Eng. Technol., pp. 1066–1071, 2022.
M. Dubey, S. V. Deo, and G. Ramtekkar, “Evaluating Properties of High Performance Concrete Containing Metakaolin as Cementitious Material,” Int. Rev. Appl. Sci. Eng., vol. 13, no. 3, pp. 257–262, 2022, doi: 10.1556/1848.2021.00359.
R. T. Lermen, P. Favaretto, R. de A. Silva, G. E. N. Hidalgo, R. M. C. Tubino, and F. Tiecher, “Effect of Additives, Cement Type, and Foam Amount on the Properties of Foamed Concrete Developed with Civil Construction Waste,” Appl. Sci., vol. 9, no. 15, 2019, doi: 10.3390/app9152998.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Redyka Sefiyanti, Zendy Bima Mahardana, Apriliya Laily Rahmawati, Nadiya Husna, Zaizafun Zakiya, Hafiizh Naufalanto, Tegar Bhakti Yuantono
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Authors who publish with this journal agree to the following terms:
(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.
(2) Publisher of U Karst is Kadiri University.
(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.