Modifikasi Beton Fc 9,8 Mpa Menggunakan Abu Ampas Kopi

Authors

  • Shirfi Wimaya Fakultas Teknik, Universitas Kadiri
  • Ahmad Ridwan Fakultas Teknik, Universitas Kadiri
  • Sigit Winarto Fakultas Teknik, Universitas Kadiri

DOI:

https://doi.org/10.30737/jurmateks.v3i2.1096

Keywords:

Ashes of Coffee Grounds, Cement, Concrete, Strong Press

Abstract

Concrete is a construction material that is widely used in building structures. Cement is the main constituent of concrete whose needs are increasing. The expansion of coffee shops in Kediri City resulted in an increase in the volume of coffee grounds waste, which can be used as an alternative to cement. The purpose of this study was to determine the value of the slump test, compressive strength test, and test the absorption capacity of the addition of coffee grounds ash to the concrete sample specimen using a cylinder is measuring 15cm x 30cm with 5 pieces of concrete quality K-125 or equivalent to fc '9.8 Mpa. Slump test results with a percentage of 4%, 8%, 12%, namely 2.5 cm, 0.5 cm and 2.5 cm. The results of the concrete compressive strength test with a percentage of 4% obtained the results of the compressive strength fc '10.51 Mpa or equivalent to K125, a percentage of 8% produces a compressive strength of fc' 8.39 and a percentage of 12% produces a compressive strength fc '7.56 Mpa equivalent to K100. The water absorption test results for 28 days resulted in an average value of 0.32 kg, 0.25 kg, 0.15 kg, and 33 kg.

Beton merupakan salah satu bahan konstruksi yang banyak digunakan pada struktur bangunan. Semen merupakan penyusun utama beton yang kebutuhannya semakin meningkat. Perluasan kedai kopi di Kota Kediri mengakibatkan peningkatan volume limbah ampas kopi yang dapat digunakan sebagai alternatif pengganti semen. Tujuan penelitian ini adalah untuk mengetahui nilai uji slump, uji kuat tekan, dan uji daya serap penambahan abu ampas kopi pada benda uji beton dengan menggunakan silinder berukuran 15cm x 30cm dengan kualitas beton sebanyak 5 buah. K-125 atau setara dengan fc '9.8 Mpa. Hasil uji slump dengan persentase 4%, 8%, 12% yaitu 2.5 cm, 0.5 cm dan 2.5 cm. Hasil uji kuat tekan beton dengan persentase 4% didapatkan hasil kuat tekan fc '10 .51 Mpa atau setara dengan K125 persentase 8% menghasilkan kuat tekan fc '8,39 dan persentase 12% menghasilkan kekuatan tekan fc '7,56 Mpa setara dengan K100. Hasil pengujian daya serap air selama 28 hari menghasilkan nilai rata-rata 0,32 kg, 0,25 kg, 0,15 kg, dan 33 kg.

References

H. Meilanda, “Pemanfaatan Serat Cangkang Kulit Kopi dalam Pembuatan Beton Polimer dengan Resin Polyester sebagai Perekat,†Repos. USU, 2018.

A. Maghfirah, E. Marlianto, and M. Iskandar, “PREPARATION AND CHARACTERIZATION OF POLYMER CONCRETE USING PUMICE AGGREGATE AND COFFEE HUSK FIBER AS A FILLER,†J. Ilmu Fis. dan Teknol., vol. 2, no. 2, pp. 1–10, 2018.

A. Ratnaningsih, R. Endah Badriani, and S. Arifin, “Pemanfaatan Limbah Kulit Kopi Sebagai Agregat Campuran Beton Ringan Material Wall/Flooring,†Repos. Unej, 2014.

Rudiatmoko, “Perancangan Struktur Gedung Beton Bertulang Menggunakan Sistem rangka Pemikul Momen Khusus (SRPMK),†J. Ilm. Elektron. Infrastruktur Tek. Sipil, vol. 1, no. 1, pp. 5–53, 2012.

Y. R. Alkhaly and M. Syahfitri, “Studi Eksperimen Penggunaan Abu Ampas Kopi Sebagai Material Pengganti Parsial Semen Pada Pembuatan Beton,†Teras J., vol. 6, no. 2, p. 101, 2017, doi: 10.29103/tj.v6i2.100.

S. Batubara and L. Simatupang, “Perencanaan Jembatan Beton Prategang Dengan Bentang 24 Meter Berdasarkan Standar Nasional Indonesia ( SNI ),†J. Rekayasa Konstr. Mek. Sipil, vol. 1, no. 2, pp. 45–61, 2018.

A. I. Candra, E. Gardjito, Y. Cahyo, and G. A. Prasetyo, “Pemanfaatan Limbah Puntung Rokok Filter Sebagai Bahan Campuran Beton Ringan Berpori,†UKaRsT, vol. 3, no. 1, p. 82, 2019, doi: 10.30737/ukarst.v3i1.365.

Y. R. Alkhaly and M. Syahfitri, “STUDI EKSPERIMEN PENGGUNAAN ABU AMPAS KOPI SEBAGAI MATERIAL PENGGANTI PARSIAL SEMEN PADA PEMBUATAN BETON,†Teras J., vol. 6, no. 2, pp. 101–110, 2016.

S. Kasus, P. Proyek, and P. Sabo, “KAJIAN KUAT TEKAN BETON DENGAN PERBANDINGAN VOLUME DAN PERBANDINGAN BERAT UNTUK PRODUKSI BETON MASSA MENGGUNAKAN AGREGAT KASAR BATU PECAH MERAPI (STUDI KASUS PADA PROYEK PEMBANGUNAN SABO DAM),†ePrints UNY, 2015.

Putra Agung Fadhilah, “Karakteristik Beton Ringan dengan Bahan Pengisi Styrofoam,†Univ. Hasanuddin Makassar, 2015.

S. Zhang, P. He, and L. Niu, “Mechanical properties and permeability of fi ber-reinforced concrete with recycled aggregate made from waste clay brick,†J. Clean. Prod., vol. 268, 2020, doi: 10.1016/j.jclepro.2020.121690.

M. D. J. Sumajouw, S. O. Dapas, and R. S. Windah, “Pengujian Kuat Tekan Beton Mutu Tinggi,†J. Ilm. Media Eng., vol. 4, no. 4, pp. 215–218, 2014.

Badan Standardisasi Nasional, “Sni 03 – 1971 – 1990,†Badan Standar Nas. Indones., 1990.

D. H. Prayogo, A. Ridwan, and S. Winarto, “PEMANFAATAN LIMBAH GYPSUM BOARD DAN BATU BATA MERAH UNTUK SUBSTITUSI SEMEN PADA PEMBUATAN BETON,†Jurmateks, vol. 2, no. 2, pp. 333–342, 2019.

F. Shabiru, “PENGGUNAAN ABU AMPAS KOPI ROBUSTA SIDIKALANG SEBAGAI SUBSTITUSI PARSIAL SEMEN TERHADAP KUAT TEKAN BETON,†Repos. Unimed, 2019.

C. W. Kusuma, “Pengaruh Variasi Penambahan Serbuk Alumunium Terhadap Kuat Tekan Beton Non Pasir Dengan Bahan Tambah Serbuk Gipsum,†Electron. Theses anda Diss. UMS, 2017, doi: 10.1080/15226510701603858.

R. Ajiono and H. Praktiko, “STABILITAS STRUKTUR TANAH JENIS EKSPANSIF MENGGUNAKAN KOMBINASI ABU DAUN,†UkaRsT, vol. 3, no. 2, pp. 13–21, 2019.

Krisnamurti, “Pengaruh Prosentase Penambahan Accelerator Terhadap Kuat Tekan Beton Normal,†Repos. Unej, 2016.

L. Bruno, “Definisi Klasifikasi Jalan,†in Journal of Chemical Information and Modeling, vol. 53, no. 9, Intergovernmental Panel on Climate Change, Ed. Cambridge: Cambridge University Press, 2019, pp. 1–30.

J. Oliver, “Improved docking of polypeptides with Glide,†J. Chem. Inf. Model., vol. 53, no. 7, pp. 1689–1699, 2013, doi: 10.1017/CBO9781107415324.004.

J. Xie, H. Zhang, L. Duan, Y. Yang, J. Yan, and D. Shan, “Effect of nano metakaolin on compressive strength of recycled concrete,†Constr. Build. Mater., vol. 256, 2020, doi: 10.1016/j.conbuildmat.2020.119393.

A. M. López, P. Fco, M. Sosa, J. Luis, and B. Senach, “Experimental study of shear strength in continuous reinforced concrete beams with and without shear reinforcement,†Eng. Struct., vol. 220, 2020, doi: 10.1016/j.engstruct.2020.110967.

Pusjatan-Balitbang PU, “SNI 03-2834-1993,†Badan Standar Nas. Indones., 1993.

F. V. Supit, R. Pandaleke, and S. O. Dapas, “Pemeriksaan Kuat Tarik Belah Beton Dengan Variasi Agregat Yang Berasal Dari Beberapa Tempat Di Sulawesi Utara,†J. Ilm. Media Eng., vol. 6, no. 2, pp. 476–484, 2016.

K. D. Kurniawan, A. Ridwan, and Y. Cahyo, “Uji Kuat Tekan dan Absorsi pada Beton Ringan dengan Penambahan Limbah Bata Ringan dan Bubuk Talek,†Jurmateks, vol. 3, no. 1, pp. 1–11, 2020.

Downloads

PlumX Metrics

Published

2020-10-30

Issue

Vol. 3 No. 2 (2020): OCTOBER

Section

Articles

License

Authors who publish with this journal agree to the following terms:

(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.

(2) Publisher of JURMATEKS is Kadiri University.

(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.