Pemanfaatan Limbah Galvalum Sebagai Substitusi Aggregat Kasar Pada Jobmix Beton

Authors

  • Muhammad Bahrudin Fakultas Teknik, Universitas Kadiri
  • Agata Iwan Candra Fakultas Teknik, Universitas Kadiri
  • Sigit Winarto Fakultas Teknik, Universitas Kadiri

DOI:

https://doi.org/10.30737/jurmateks.v3i2.1152

Keywords:

Compressive Strength, Concrete, Rough Aggregate, Waste

Abstract

Concrete is one of the construction materials that is widely used. Currently, variations in concrete are being studied. Galvalum waste has high tensile properties but is mild. Its lightweight properties are expected to reduce the weight of the concrete itself. The purpose of this study is to find out the value of strong press, absorption, weight type (E), degree of saturation (Sr), moisture content (Wc), and porosity of the addition of galvalume waste. The method used is a experimental method. Variations in galvalum waste substitution used are 50% and 100% of the aggregate weight is roughT the sample used in the form of a cylinder size of 15cm x 30 cm with the initial quality of fc' 18.67 Mpa. The results of the strong press test showed that the galvalum waste subtitution has not been able to exceed the initial quality of the plan. The highest test result was obtained at a percentage of 50% with a strong press score of FC' 17.94 Mpa. In the percentage, absorption test results are 0.010%, the weight of the type is 2325 kg / m3, the pore number is 0.00232%, the water content is 0.108%, and porosity is 0.00108%.

Beton merupakan salah satu bahan konstruksi yang banyak dipergunakan. Saat ini, pengguanaan variasi pada beton sedang banyak diteliti. Limbah galvalum memiliki sifat tarik yang tinggi namun ringan. Sifatnya yang ringan diharapkan mampu mengurangi berat beton itu sendiri. Tujuan dari penelitian ini adalah untuk mengetahui nilai kuat tekan, absorpsi, berat jenis (Ɣ), angka pori (e),derajat kejenuhan (Sr), kadar air (Wc), dan porositas dari penambahan limbah galvalum. Metode yang digunakan merupakan metode eksperimen. Variasi pensubtitusi limbah galvalum yang digunakan yaitu 50% dan 100% dari berat agregat kasar. sampel yang digunakan berbentuk silinder ukuran 15cm x 30 cm dengan mutu awal fc’ 18.67 Mpa. Hasil uji kuat tekan menunjukkan bahwa subtitusi limbah galvalum belum mampu melebihi mutu awal rencana. Hasil uji tertinggi didapat pada prosentase 50% dengan nilai kuat tekan fc’ 17,94 Mpa. Pada prosentase tersebut, didapat hasil uji absropsi yaitu 0,010%,  berat jenis yaitu 2325 kg/m3, angka pori yaitu 0,00232%, kadar air yaitu 0,108% serta porositas yaitu 0,00108%.

 

References

S. Needhidasan and P. Sai, “Demonstration on the limited substitution of coarse aggregate with the E-waste plastics in high strength concrete,†Mater. Today Proc., vol. 22, pp. 1004–1009, 2020, doi: 10.1016/j.matpr.2019.11.255.

L. Bruno, “Kajian Kuat Tekan Beton Normal Menggunakan Standar SNI 7656-2012 Dan ASTM C 136-06,†J. Chem. Inf. Model., vol. 53, no. 9, pp. 1689–1699, 2019, doi: 10.1017/CBO9781107415324.004.

A. I. Candra and E. Siswanto, “Rekayasa Job Mix Beton Ringan Menggunakan Hydroton Dan Master Ease 5010,†J. CIVILA, vol. 3, no. 2, pp. 162–165, 2018.

N. Suprihatin, “Tinjauan Kuat Tekan Dan Kuat Tarik Belah Beton Dengan Serat Kawat Bendrat Berbentuk ‘W’ Sebagai Bahan Tambah,†J. Teknol., vol. 1, no. 1, pp. 69–73, 2013, doi: 10.11113/jt.v56.60.

E. J. Aprizal and P. Prapto, “Pengaruh Partial Replacement Semen Portland Dengan Bentonite Terhadap Kuat Tekan Beton Berdasarkan Variasi Umur,†Inf. dan Ekspose Has. Ris. Tek. Sipil dan Arsit., vol. 11, no. 1, pp. 67–78, 2015.

R. Irmawaty and A. A. Muhaimin, “Studi Perilaku Mekanik Beton Dengan Crumb Rubber,†Univ. Hasanuddin. Gowa Makasar, 2015.

Y. Rismayasari, U. U, and U. Santosa, “Pembuatan Beton dengan Campuran Limbah Plastik dan Karakterisasinya,†Indones. J. Appl. Phys., vol. 2, no. 02, p. 24, 2016, doi: 10.13057/ijap.v2i02.1284.

P. Gunawan and Setiono, “Foamed lightweight concrete tech using galvalum Az 150 fiber,†Procedia Eng., vol. 95, no. Scescm, pp. 433–441, 2014, doi: 10.1016/j.proeng.2014.12.203.

G. O. Bamigboye, O. Okara, D. E. Bassey, K. J. Jolayemi, and D. Ajimalofin, “The use of Senilia senilis seashells as a substitute for coarse aggregate in eco-friendly concrete,†J. Build. Eng., vol. 32, no. September, p. 101811, 2020, doi: 10.1016/j.jobe.2020.101811.

W. I. Dharmawan, D. Oktarina, and M. Safitri, “Perbandingan Nilai Kuat Tekan Beton Menggunakan Hammer Test dan Compression Testing Machine terhadap Beton Pasca Bakar,†Media Komun. Tek. Sipil, vol. 22, no. 1, p. 35, 2016, doi: 10.14710/mkts.v22i1.12404.

S. Zuraidah, “PENGARUH PENGGUNAN LIMBAH PAVING SEBAGAI ALTERNATIF AGREGAT KASAR UNTUK BETON,†J. Ilm. Kern, vol. 2, no. 2, pp. 69–72, 2012, doi: 10.1080/15226510701603858.

M. Farhan, “Penambahan Abu Batubara sebagai Bahan Campuran untuk Proses Pembuatan Semen,†Diss Politek. Negeri Sriwij., 2016.

D. Haryanto, “Pemanfaatan Limbah Senyawa Lateks Karet Alam pada Beton Polimer dengan Pengisi Serbuk Cangkang Telur Ayam dan Pengeras Poliester,†Repos. USU, 2018.

K. Srinivas, S. Kranthi Vijaya, and K. Jagadeeswari, “Concrete with ceramic and granite waste as coarse aggregate,†Mater. Today Proc., pp. 7–10, 2020, doi: 10.1016/j.matpr.2020.07.521.

E. Gardjito, A. I. Candra, and Y. Cahyo, “Pengaruh Penambahan Batu Karang Sebagai Substitusi Agregat Halus Dalampembuatan Paving Block,†UKaRsT, vol. 2, no. 1, pp. 36–42, 2018.

A. I. Candra, H. Wahyudiono, S. Anam, and D. Aprillia, “KUAT TEKAN BETON Fc ’ 21 ,7 MPa MENGGUNAKAN WATER REDUCING AND HIGH RANGE ADMIXTURES,†J. CIVILA, vol. 5, no. 1, pp. 330–339, 2020.

A. V. Rahul and M. Santhanam, “Evaluating the printability of concretes containing lightweight coarse aggregates,†Cem. Concr. Compos., vol. 109, no. February, p. 103570, 2020, doi: 10.1016/j.cemconcomp.2020.103570.

A. I. Candra, E. Gardjito, Y. Cahyo, and G. A. Prasetyo, “Pemanfaatan Limbah Puntung Rokok Filter Sebagai Bahan Campuran Beton Ringan Berpori,†UKaRsT, vol. 3, no. 1, p. 82, 2019, doi: 10.30737/ukarst.v3i1.365.

R. C. Ardhisa, R. M. Maladzi, P. Sabdono, D. T. Sipil, F. Teknik, and U. Diponegoro, “Penggunaan bekisting galvalum bergelombang sebagai tulangan eksternal pada balok beton bertulang,†J. karya Tek. sipil, vol. 6, 2017.

Badan Standardisasi Nasional, “SNI 031973-2016 Metode uji Densitas, Volume Produksi Campuran Dan Kadar Udara (Gravimetrik) Beton,†2016.

S. Hidayat, “Tinjauan Kuat Tekan dan Kuat Tarik Belah Beton dengan Sebagian Semen Diganti Tanah Pozolan dari Kecamatan Tulakan,†Diss Univ. Muhamadiyah Surakarta, 2014.

Badan Standardisasi Nasional, “SNI 03-1974-1990 Metode Pengujian Kuat Tekan Beton,†1990.

Downloads

PlumX Metrics

Published

2020-10-30

Issue

Vol. 3 No. 2 (2020): OCTOBER

Section

Articles

License

Authors who publish with this journal agree to the following terms:

(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.

(2) Publisher of JURMATEKS is Kadiri University.

(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.