PEMANFAATAN SERBUK KACA DARI JENIS KACA BENING DENGAN KETEBALAN 3-4 MM SEBAGAI BAHAN TAMBAH DALAM PEMBUATAN BATAKO
DOI:
https://doi.org/10.30737/jurmateks.v1i1.139Keywords:
Brick, Compressive Strength, Water Absorption, Glass PowderAbstract
Batako is a building material to replace brick, which is composed of sand, portland cement, and water. This type of research is an experimental study in the form of compressive strength testing with the addition of glass powder. We are planning a mixture of brick making materials with a ratio of 1: 6 cement and sand. Making the test object size and external appearance and testing the absorption capacity using a mortar specimen measuring 5 x 5 x 5 cm. Variations in adding glass powder by reducing the amount of sand starting from 0%, 10%, 15%, 20%, and 25% of the weight of the sand. Testing of the mechanical properties of the brick was carried out at the age of 7, 14, and 28 days for the compressive strength test of the brick, and 28 days for the absorption test of the brick. The compressive strength of the concrete blocks increases with age. From the test, it was concluded that the most optimum mixture was the concrete block with a mixture concentration of 25%, namely 58.00 kg / cm² for the results of the concrete block compressive strength test and 11.19 grams for the brick absorption test.
Batako merupakan bahan bangunan pengganti batu bata yang tersusun dari pasir, semen portland dan air. Jenis penelitian ini adalah penelitian eksperimen berupa pengujian kuat tekan dengan penambahan serbuk kaca. Perencanaan campuran bahan penyusun batako dengan perbandingan 1 : 6 semen dan pasir. Pembuatan benda uji ukuran dan tampak luar dan pengujian daya serap menggunakan benda uji mortar ukuran 5 x 5 x 5 cm. Variasi penambahan serbuk kaca dengan mengurangi jumlah pasir mulai dari 0%, 10%, 15%, 20%, dan 25% dari berat pasir. Pengujian sifat mekanik batako dilakukan pada umur 7, 14, dan 28 hari untuk uji kuat tekan batako, dan 28 hari untuk uji penyerapan batako. Kuat tekan batako meningkat seiring dengan bertambahnya umur. Dari pengujian disimpulkan bahwa campuran yang paling optimum adalah batako dengan konsentrasi campuran 25% yaitu 58.00 kg/cm² untuk hasil uji kuat tekan batako dan 11.19 gram untuk uji serapan batako.
References
C. Habsya, A. Rahmawati, and S. Sumarni, “Lockbrick Modular Beton Untuk Alternatif Bahan Dinding,†sinektika, vol. 14, no. 2, pp. 234–242, 2004.
L. Wibowo, “Pengaruh penambahan serbuk kaca dan WATER REDUCING HIGH RANGE ADMIXTURES TERHADAP KUAT DESAK DAN MODULUS ELASTISITAS PADA BETON,†2013.
B. S. Nasional, “Sni 03-0349-1989,†Bata Bet. untuk pasangan dinding, 1989.
H. Mallisa, “Studi Kelayakan Kualitas Batako Hasil Produksi Industri Kecil di Kota Palu,†Media Litbang Sulteng, vol. 4, no. 2, pp. 75–82, 2011.
Badan Standardisasi Nasional, “SNI 03-0691-1996 Bata Beton.â€
G. Gunawan, P. Nawangsari, and D. Masnur, “STUDI PEMANFAATAN LIMBAH KACA DAN PISTON BEKAS SEBAGAI MATERIAL ALTERNATIF KANVAS REM SEPEDA MOTOR DENGAN MENGGUNAKAN METODE METALURGI SERBUK,†Jom FTEKNIK, vol. 3, no. 2, pp. 1–6, 2016.
Ristinah, A. Zacoeb, A. Soehardjono, and D. Setyowulan, “Pengaruh Penggunaan Bottom Ash Sebagai Pengganti Semen Pada Campuran Batako Terhadap Kuat Tekan Batako,†Rekayasa Sipil, vol. 6, no. 3, pp. 264–271, 2012.
Rahmat, I. Hendriyani, and R. Sa’diyah, “ANALISIS BATAKO DENGAN CAMPURAN SERBUK KACA SEBAGAI PENGGANTI PASIR.â€
B. Herbudiman and C. Januar, “PEMANFAATAN SERBUK KACA SEBAGAI POWDER PADA SELF-COMPACTING CONCRETE,†2011.
I. Handayasari, “STABILISASI TANAH PADA LAHAN BEKAS TEMPAT PEMBUANGAN AKHIR (TPA) SAMPAH DENGAN PEMANFAATAN SERBUK LIMBAH BOTOL KACA SEBAGAI BAHAN CAMPURAN.â€
Kosim and A. Hasan, “Pemanfaatan Serbuk Kaca Sebagai Bahan Tambah Agregat Halus Untuk Meningkatkan Kuat Tekan Beton,†J. Tek. Sipil, vol. 10, no. 2, pp. 170–178, 2014.
H. Purnomo and E. S. Hisyam, “PEMANFAATAN SERBUK KACA SEBAGAI SUBSTITUSI PARSIAL SEMEN PADA CAMPURAN BETON DITINJAU DARI KEKUATAN TEKAN DAN KEKUATAN TARIK BELAH BETON,†J. Fropil, vol. 2, no. 1, pp. 45–55, 2014.
Nursyamsi, I. Indrawan, and I. P. Hastuty, “PEMANFAATAN SERBUK KACA SEBAGAI BAHAN TAMBAH DALAM PEMBUATAN BATAKO,†2016.
A. A. F. Putra, “Karakteristik Beton Ringan dengan Bahan Pengisi Styrofoam,†2015.
SNI 4431:2011, “Cara uji kuat lentur beton normal dengan dua titik pembebanan,†Standar Nas. Indones., p. 16, 2011.
M. A. Punusingon, B. D. Handono, and R. Pandaleke, “UJI EKSPERIMENTAL KUAT TEKAN BETON DAUR ULANG DENGAN BAHAN TAMBAH ABU TERBANG (FLY ASH) DAN SERBUK KACA SEBAGAI SUBSTITUSI PARSIAL SEMEN,†Sipil Statik.
N. Rasif, I. S. Dewi, N. Aviani, and W. Utama, “ANALISIS KUAT TEKAN DAN DENSITAS BETON NON-PASIR DENGAN CAMPURAN VARIAN ABU TERBANG MENGGUNAKAN MATLAB,†PROKONS.
D. P. Kusumastuti, I. Sepriyanna, and Hastanto, “Perubahan Angka Pori Tanah Lunak Terstabilisasi dengan serbuk kaca dan serat karung plastik,†Semnastek.
Badan Standarisasi Nasional, “SNI 7656-2012 Tata Cara Pemilihan Campuran Beton Normal, Beton Berat, dan beton Massa,†2012.
M. Ramadhan, Budiono, and T. P. Artiningsih, “PENGARUH PROSES CURING DENGAN CARA PERENDAMAN DALAM AIR MENDIDIH TERHADAP BETON REAKTIF SEMEN,†pp. 1–11.
Downloads
Issue
Section
License
Authors who publish with this journal agree to the following terms:
(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.
(2) Publisher of JURMATEKS is Kadiri University.
(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.