STUDI EXPERIMEN KUAT TEKAN BETON DENGAN MEMANFAATKAN LIMBAH KERAMIK DAN BATA MERAH
DOI:
https://doi.org/10.30737/jurmateks.v2i1.394Keywords:
Concrete, Red Brick, Ceramic Waste, Compressive StrengthAbstract
Normal concrete sample (1) has a compressive strength of 222.22 kg/cm, normal concrete (2) has a compressive strength of 242.933 kg/cm, concrete using a mixture of ceramic 21% and red brick 7% sample (1) has a compressive strength of 177.911 kg/cm, concrete using a mixture of 21% Ceramics and red brick 7% sample (2) has a compressive strength of 189.777 kg/cm, concrete using a mixture of 10% Ceramics and red brick 4% sample (1) has a compressive strength of 204.667 kg/cm, concrete which uses a mixture of 10% Ceramics and red brick 4% sample (2) has a compressive strength of 137,333 kg/cm. It shows that the compressive strength of concrete decreases from increasing the volume of ceramics because the ceramic surface cannot bind perfectly. The highest K-204,667 with a mixture of 10% ceramics and 4% red brick and 28-day-old concrete, while to reach the K-250, is very far away. Of the 6 samples, the average reached K-195,807.
Sampel beton normal (1) memiliki kuat tekan 222,22 kg / cm, beton normal (2) memiliki kuat tekan 242.933 kg / cm, sampel beton menggunakan campuran keramik 21% dan bata merah sampel 7% (1) memiliki kuat tekan 177.911 kg / cm, sampel beton menggunakan campuran keramik 21% dan bata merah 7% (2) memiliki kuat tekan 189.777 kg / cm, sampel beton campuran 10% Keramik dan bata merah 4% (1) kuat tekan 204.667 kg / cm, sampel beton yang menggunakan campuran Keramik 10% dan sampel bata merah 4% (2) memiliki kuat tekan 137.333 kg / cm. Ini menunjukkan bahwa Kuat tekan beton semakin berkurang dari bertambahnya volume keramik, karena permukaan keramik tidak bisa mengikat dengan sempurna. K-204.667 tertinggi dengan campuran 10% keramik dan 4% bata merah serta beton berumur 28 hari, sedangkan untuk mencapai K-250 sangat jauh jauh. Dari 6 sampel tersebut rata-rata mencapai K-195.807.
References
A. I. Candra and E. Siswanto, “Rekayasa Job Mix Beton Ringan Menggunakan Hydroton Dan Master Ease 5010,†J. CIVILA, vol. 3, no. 2, p. 162, 2018, doi: 10.30736/cvl.v3i2.258.
M. M. Amin, A. D. Limantara, and S. Winarto, “UJI LABORATORIUM PEMANFAATAN BIO ENZIM (BIOCONC) SEBAGAI PEREDUKSI SEMEN PADA BATA BETON MUTU A,†Jurmateks, vol. 1, no. 1, pp. 56–65, 2018.
T. Mulyono, “TEKNOLOGI BETON: Dari Teori Ke Praktek,†no. October 2018, p. 574, 2015.
A. Y. Bintoro, A. D. Limantara, and S. Winarto, “EVALUASI KEKUATAN CONCBLOCK DENGAN AGREGAT HALUS DAN AGREGAT KASAR DARI TEMPURUNG KELAPA,†Jurmateks, vol. 1, no. 1, pp. 160–171, 2018.
Badan Standardisasi Nasional, “SNI 03-2834-2000 Tata Cara Pembuatan Rencana Campuran Beton Normal,†2000.
D. Hartanto, Y. Cahyo, S. Winarto, and A. I. Candra, “PERENCANAAN PONDASI TIANG PANCANG PADA GEDUNG SEKRETARIAT DEWAN DPRD KABUPATEN KEDIRI,†Jurmateks, vol. 1, no. 2, pp. 303–312, 2018.
Badan Standardisasi Nasional, “SNI 1974:2011 Cara Uji Kuat Tekan Beton dengan Benda Uji Silinder,†2011.
Badan Standardisasi Nasional, “SNI 3402:2008 Cara Uji Berat Isi Beton Ringan Struktural,†2008.
T. P. G. A, Y. C. S. P, S. Winarto, and A. I. Candra, “PERBANDINGAN KEKUATAN BETON DENGAN CAMPURAN DRAMIX STEEL FIBER DAN TULANGAN WIREMESH PADA RIGID PAVEMENT,†Jurmateks, vol. 1, no. 2, pp. 313–324, 2018.
K. Tjokrodimuljo, “Teknologi Beton,†Biro Penerbit Tek. Sipil Univ. Gajah Mada, 2009.
Badan Standarisasi Nasional, “SNI 2847:2013 Persyaratan Beton Struktural untuk Bangunan Gedung,†2013.
Badan Standarisasi Nasional, “SNI 03-1750-1990 Mutu dan Cara Uji Agregat Beton,†1990.
ASTM 128, “Standard Test Method for Relative Density ( Specific Gravity ) and Absorption of Fine Aggregate,†pp. 1–6, 2016.
Badan Standardisasi Nasional, “SNI 2493:2011 Tata Cara Pembuatan dan Perawatan Benda Uji Beton di Laboratorium,†2011.
ASTM, “Annual Book of ASTM Standart Volume 04.02 ‘Concrete and Aggregates,’†no. October 1965, 2003.
ASTM C 187, “Normal Consistency of Hydraulic Cement,†pp. 10–12.
E. Gardjito, A. I. Candra, and Y. Cahyo, “Pengaruh Penambahan Batu Karang Sebagai Substitusi Agregat Halus Dalam Pembuatan Paving Block,†UKaRsT, vol. 2, no. 1, p. 35, 2018, doi: 10.30737/ukarst.v2i1.374.
ASTM C 188 - 09, “Standard Test Method for Density of Hydraulic Cement,†vol. i, pp. 1–3, 2010, doi: 10.1520/C0188-09.2.
ASTM C 127, “Standard Test Method for Density, Relative Density (Specific Gravity), and Absorption of Coarse Aggregate,†pp. 3–8, 2001.
ASTM C 29, “Standard Test Method for Bulk Density (‘ Unit Weight ’) and Voids in Aggregate,†vol. 97, no. Reapproved, pp. 3–6, 2003.
ASTM C 39, “Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens,†vol. 04, no. March, pp. 1–5, 2001.
ASTM C 33, “Standard Specification for Concrete Aggregates,†vol. 04, 2001.
JIS A 1148:2010, “Method of Test for Resistance of Concrete to Freeze and Thawing.†.
ASTM 191, “Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle,†no. C, pp. 1–8, 2010, doi: 10.1520/C0191-08.2.
Downloads
Published
Issue
Section
License
Authors who publish with this journal agree to the following terms:
(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.
(2) Publisher of JURMATEKS is Kadiri University.
(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.