Menentukan Proporsi Campuran Mortar yang Tepat dengan Pemanfaatan Limbah Fly Ash dan Bottom Ash Ditinjau dari Kuat Tekan
DOI:
https://doi.org/10.30737/jurmateks.v5i2.3635Keywords:
Bottom Ash, Compressive Strength, Fly Ash, Mortar, Oxidation ConcentrationAbstract
The increase in the amount of fly ash and bottom ash waste every year requires proper management and utilization. In the manufacture of concrete, the use of fly ash and bottom ash can be used as a substitute material. However, it has not been utilized in making species in construction. This is because the exact proportion has not been obtained. The purpose of this study was to determine the correct proportions in the mortar with a mixture of fly ash and bottom ash. The research was carried out using experimental methods in the laboratory with cube-shaped specimens (5 x 5 x 5 cm) with 2 kinds of ratios between binder and fine aggregate, namely 1:2 and 1:4, each having a different percentage of sand and bottom ash, starting from from 20% to 80%. While the fly ash used is 10%. Tests carried out included material tests (Metal Oxidation Concentration Test and Sieve Analysis), and compressive strength tests (14 and 28 days). The results showed that the highest mortar compressive strength was at a ratio of 1:2 with fly ash as a cement mixture of 10% and bottom ash as a sand mixture of 20% with a compressive strength value of 16.8 MPa at the age of the specimen 28 days. The compressive strength value is in accordance with the provisions of SNI 03-6825-2002. The results of this study can be used by the community in making plaster work and can reduce the amount of waste that exists today.References
K. E. Ghozali, A. Yonathan, A. Antoni, and D. Hardjito, “Penelitian Awal Pemanfaatan Fly Ash dan Bottom Ash PLTU Suralaya Dalam Pembuatan Beton Di Lingkungan Pantai,†J. Dimens. Pratama Tek. Sipil, vol. 7, no. 2, pp. 177–184, 2018.
M. Qomaruddin, Y. A. Saputro, and S. Sudarno, “Kajian Penggunaan Bottom Ash sebagai Mortar Beton,†Pros. SNST ke-9 Univ. Wahid Hasyim Semarang, pp. 34–39, 2018.
M. A. Sultan and R. Sakti, “Subtitusi Partitusi Agregat Halus Dengan Bottom Ash Pada Pembuatan Bata Semen,†Rekayasa Sipil, vol. 13, no. 1, pp. 64–69, 2019, doi: 10.21776/ub.rekayasasipil.2019.013.01.9.
N. Ngudiyono, N. N. Kencanawati, and R. Prakarsa, “Pemanfaatan Fly Ash sebagai Bahan Subtitusi Parsial Semen pada Beton Memadat Sendiri,†J. Teknol. Lingkung., vol. 23, no. 1, pp. 055–061, 2022, doi: 10.29122/jtl.v23i1.5130.
Kusdiyono, Supriyadi, and H. L. Wahyono, “Pengaruh Penambahan Fly Ash dan Bottom Ashpada Pembuatan Beton Mutu F’c 20 Mpa dalam Upaya Pemanfaatan Limbah Industri,†Wahana Tek. SIPIL, vol. 22, no. 1, pp. 40–49, 2017, doi: http://dx.doi.org/10.32497/wahanats.v22i1.899.
R. A. Wijaya, S. Wijayanti, and Y. Astuti, “Fly Ash Limbah Pembakaran Batubara sebagai Zat Mineral Tambahan (Additive) untuk Perbaikan Kualitas dan Kuat Tekan Semen,†Media Komun. Tek. Sipil, vol. 27, no. 1, pp. 127–134, 2021.
M. Qomaruddin, A. Ariyanto, Y. A. Saputro, and S. Sudarno, “Analisa Kuat Tekan Mortar Beton Fly Ash Dari Industri Pltu Tanjung Jati Jepara Dengan Menggunakan Pasir Sungai Tempur Kabupaten Jepara,†Rev. Civ. Eng., vol. 2, no. 1, pp. 35–40, Mar. 2018, doi: 10.31002/rice.v2i1.678.
A. Susilowati and T. Oktaviana, “Pengaruh Variasi Bottom Ash terhadap Sifat Fisik dan Sifat Mekanik pada Mortar Semen,†RekaRacana J. Tek. Sipil, vol. 7, no. 3, p. 139, 2021, doi: 10.26760/rekaracana.v7i3.139.
R. Yanuari et al., “Studi Parametrik Mortar Geopolimer Hybrid Abu Sawit (Palm Oil Fuel Ash / Pofa),†Rekayasa Sipil, vol. 14, no. 2, pp. 83–90, 2020, doi: 10.21776/ub.rekayasasipil.2020.014.02.1.
H. Wu, Y. Jia, Z. Yuan, Z. Li, T. Sun, and J. Zhang, “Study on the Mechanical Properties, Wear Resistance and Microstructure of Hybrid Fiber-Reinforced Mortar Containing High Volume of Industrial Solid Waste Mineral Admixture,†Materials (Basel)., vol. 15, no. 11, 2022, doi: 10.3390/ma15113964.
M. Saukani and S. Arief, “Karakteristik Termal Mortar Geopolimer Berbasis Abu Layang dan Kaolin Alam,†Jurnal Fisika Flux, vol. 15, no. 2, pp. 139–142, 2019, doi: 10.20527/flux.v15i2.5534.
J. Gulicovski, N. Risti, and S. Mili, “Waste slag from heating plants as a partial replacement for cement in mortar and concrete production. Part i—physical–chemical and physical–mechanical characterization of slag,†pp. 1–15, 2020, doi: 10.3390/min10110992.
M. Qomaruddin, K. Umam, I. Istianah, Y. Adi Saputro, and P. Purwanto, “Pengaruh Bahan Kalsium Oksida pada Waktu Pengikatan Pasta Beton Geopolimer dan Konvensional,†Eksakta J. Sci. Data Anal., vol. 19, pp. 182–192, 2019, doi: 10.20885/eksakta.vol19.iss2.art8.
X. Ding, T. Ma, L. Gu, and Y. Zhang, “Materials & Design Investigation of surface micro-crack growth behavior of asphalt mortar based on the designed innovative mesoscopic test,†Mater. Des., vol. 185, p. 108238, 2020, doi: 10.1016/j.matdes.2019.108238.
J. Li, H. Zhou, W. Chen, and Z. Chen, “Shear properties of a new type recycled aggregate concrete interlocking hollow block masonry with axial load,†pp. 1–15, 2021, doi: 10.1177/13694332211012568.
G. Vu, T. Iskhakov, J. J. Timothy, C. Schulte-Schrepping, R. Breitenbücher, and G. Meschke, “Cementitious composites with high compaction potential: Modeling and calibration,†Materials (Basel)., vol. 13, no. 21, pp. 1–17, 2020, doi: 10.3390/ma13214989.
Wahyuni E. T., Supraba D, Raharjo S, and Siswanta D, “Kajian Metode foto-Fenton untuk Penurunan Konsentrasi Ion Logam Berat Pb(II) dan Cu(II) dalam Larutan Secara Simultan dan Sinergi,†J. Kim. Sains dan Apl., vol. 22, no. 5, pp. 192–199, 2019, doi: 10.14710/jksa.22.5.192-199.
M. Wiyono and W. Wahyudi, “Analisis Unsur dalam Fly Ash dari Industri PLTU Batubara dengan Metode Analisis Aktivasi Neutron,†J. Teknol. Lingkung., vol. 19, no. 2, p. 221, 2018, doi: 10.29122/jtl.v19i2.2778.
R. Damayanti, “Abu batubara dan pemanfaatannya: Tinjauan teknis karakteristik secara kimia dan toksikologinya,†J. Teknol. Miner. dan Batubara, vol. 14, no. 3, pp. 213–231, 2018, doi: 10.30556/jtmb.vol14.no3.2018.966.
D. N. Wahono, Z. Arifin, Y. C. S. Poernomo, Z. B. Mahardana, and A. Yamin, “Kuat Tekan dan Penyerapan Batako Menggunakan Serat Pelepah Kelapa,†J. Manaj. Teknol. Tek. Sipil, vol. 4, no. 2, p. 86, 2021, doi: 10.30737/jurmateks.v4i2.2016.
M. Felix Wijaya, M. Olivia, and E. Saputra, “Kuat Tekan Mortar Geopolimer Abu Terbang Hybrid menggunakan Semen Portland,†J. Tek., vol. 13, no. 1, pp. 60–68, 2019, doi: 10.31849/teknik.v13i1.2914.
E. Riyanto, E. Widyananto, and R. R. Renaldy, “Analisis Kuat Tekan Mortar Geopolimer Berbahan Silica Fume dan Kapur Tohor,†INERSIA lNformasi dan Ekspose Has. Ris. Tek. SIpil dan Arsit., vol. 17, no. 1, pp. 19–26, 2021, doi: 10.21831/inersia.v17i1.35901.
A. J. Khan et al., “Axial compressive behavior of reinforced concrete (Rc) columns incorporating multi-walled carbon nanotubes and marble powder,†Crystals, vol. 11, no. 3, pp. 1–16, 2021, doi: 10.3390/cryst11030247.
H. Zhang, J. Liu, B. Wu, and Z. Zhang, “Axial Compressive Behavior of Geopolymer Recycled,†Materials (Basel), vol. 13, no.3, pp. 1–16, 2020, doi: 10.3390/ma13030533.
A. Salinas and D. Feys, “Estimation of Lubrication Layer Thickness and Composition through Reverse Engineering of Interface Rheometry Tests,†Materials, vol. 13, no. 8, p 1799, 2020, doi: 10.3390/MA13081799.
Downloads
Published
Issue
Section
License
Authors who publish with this journal agree to the following terms:
(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.
(2) Publisher of JURMATEKS is Kadiri University.
(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.