Pengujian Kuat Tekan Pada Beton Dengan Penambahan Limbah Marmer Dan Serat Batang Pisang
DOI:
https://doi.org/10.30737/jurmateks.v3i2.1150Keywords:
Banana Rod Fiber, Marble Waste, Strong PressAbstract
In the era of technological developments, concrete is one of the primary components of a construction that takes year to unfold. Thus  needs to be innovation of concrete making materials. These additional material are marble waste and banana rod fibers. Marble waste is a waste from the manufacture of ornamental stone whose waste can utilized for concrete making mixture materials. While banana rod are environmental waste that is not utilized properly. The aim of this study is to find out the effect of adding marble waste and banana stem fibers to the strong value of concrete press and slump, with a percentage of 10%, 20%, 30% of the rough aggregate weight. Strong press testing was carried out at 28 days concrete life with an initial quality of FC' 18.68 Mpa. The results showed that the highest press strength was obtained from the addition of marble waste and banana stem fiber at a percentage of 10% which is 17.94 Mpa. The conclusion of this study strongly press experienced a decrease from percentage 10%, 20%, 30% sequentially.
Di era perkembangan teknologi, beton merupakan salah satu komponen utama dalam sebuah konstruksi yang dimana disetiap tahunnya mengalami perkembangan pesat. Dengan begitu perlu adanya  inovasi dari bahan pembuatan beton. Bahan tambahan tersebut merupakan limbah marmer dan serat batang pisang. Limbah marmer merupakan limbah dari pembuatan batu hias yang limbahnya mampu dimanfaatkan untuk bahan campuran pembuatan beton sedangkan serta batang pisang merupakan limbah lingkungan yang tidak dimanfaatkan dengan baik. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh penambahan limbah marmer dan serat batang pisang terhadap nilai kuat tekan dan slump beton , dengan prosentase 10%, 20%, 30% dari berat agregat kasar. Pengujian kuat tekan dilakukan pada umur beton 28 hari dengan mutu awal fc’ 18,68 Mpa. Hasil penelitian menunjukkan bahwa kuat tekan tekan tertinggi diperoleh dari penambahan limbah marmer dan serat batang pisang pada prosentase 10% yaitu 17,94 Mpa. Kesimpulan dari penelitian ini kuat tekan mengalami penurunan dari prosentase 10%, 20%, 30% secara berurutan.
References
H. Bardosono and B. Herbudiman, “Beton Daur Ulang Variasi campuran beton,†vol. 4, pp. 2–3, 2010.
E. W. Setyowati, “Kuat Tekan Beton Limbah Batu Onix Tulungagung,†J. Media Tek. Sipil, vol. 14, no. 2, p. 140, 2016, doi: 10.22219/jmts.v14i2.3703.
J. He and X. Shi, “Accelerated Laboratory Assessment of Discrete Sacrificial Anodes for Rehabilitation of Salt-Contaminated Reinforced Concrete,†J. Mater. Civ. Eng., vol. 32, no. 11, p. 04020344, 2020, doi: 10.1061/(asce)mt.1943-5533.0003374.
E. Hunggurami, M. E. Bolla, and P. Messakh, “Perbandingan Desain Campuran Beton Normal Menggunakan Sni 03-2834-2000 Dan Sni 7656: 2012,†J. Tek. Sipil, vol. 6, no. 2, pp. 165–172, 2017.
S. Ghosn, N. Cherkawi, and B. Hamad, “Studies on Hemp and Recycled Aggregate Concrete,†Int. J. Concr. Struct. Mater., vol. 14, no. 1, 2020, doi: 10.1186/s40069-020-00429-6.
E. Siswanto, “Penambahan Fly Ash Dan Serat Serabut Kelapa Sebagai Bahan Pembuatan Beton,†UKaRsT, vol. 3, no. 1, p. 48, 2019, doi: 10.30737/ukarst.v3i1.352.
B. Tiwari, B. Ajmera, R. Maw, R. Cole, D. Villegas, and P. Palmerson, “Mechanical properties of lightweight cellular concrete for geotechnical applications,†J. Mater. Civ. Eng., vol. 29, no. 7, pp. 1–7, 2017, doi: 10.1061/(ASCE)MT.1943-5533.0001885.
A. F. Kariri and N. A. Affandy, “ANALISIS KUAT TEKAN BETON DENGAN BAHAN TAMBAH PELEPAH PISANG PADA BETON MUTU K-200,†UKaRsT, vol. 2, no. 2, pp. 115–124, 2018.
M. Ibrahim, A. Ahmad, M. S. Barry, L. M. Alhems, and A. C. Mohamed Suhoothi, “Durability of Structural Lightweight Concrete Containing Expanded Perlite Aggregate,†Int. J. Concr. Struct. Mater., vol. 14, no. 1, 2020, doi: 10.1186/s40069-020-00425-w.
Rusdianto, Yunan, and M. Munir, “Penggunaan Limbah Marmer Sebagai Filler Terhadap Absorbsi, Kuat Tekan dan Modulus Elastisitaas pada Beton,†Media Tek. Sipil, vol. 13, no. 1, pp. 99–108, 2015.
X. Zou and L. H. Sneed, “Bond Behavior Between Steel Fiber Reinforced Polymer (SRP) and Concrete,†Int. J. Concr. Struct. Mater., vol. 14, no. 1, pp. 1–17, 2020, doi: 10.1186/s40069-020-00420-1.
A. I. Candra, H. Wahyudiono, S. Anam, and D. Aprillia, “KUAT TEKAN BETON Fc ’ 21 ,7 MPa MENGGUNAKAN WATER REDUCING AND HIGH RANGE ADMIXTURES,†J. CIVILA, vol. 5, no. 1, pp. 330–339, 2020.
A. I. Candra, A. Ridwan, S. Winarto, and Romadhon, “Correlation of Concrete Strength and Concrete Age K-300 Using Sikacim® Concrete Additive and Master Ease 5010,†J. Phys. Conf. Ser., vol. 1569, no. 4, 2020, doi: 10.1088/1742-6596/1569/4/042032.
S. Supraptiningsih, “Pengaruh serbuk serat batang pisang sebagai filler terhadap sifat mekanis dari komposit PVC– CaCO3,†Maj. Kulit, Karet, dan Plast., vol. 28, no. 2, p. 79, 2012, doi: 10.20543/mkkp.v28i2.108.
S. Hani and . R., “Pengaruh Campuran Serat Pisang Terhadap Beton,†Educ. Build., vol. 4, no. 1, pp. 40–45, 2018, doi: 10.24114/eb.v4i1.10043.
A. Salam and S. D. Hartantyo, “Pengaruh Penambahan Serat Pelepah Pisang Pada Pembuatan Paving Block K-175,†J. CIVILA, vol. 2, no. 2, p. 8, 2017, doi: 10.30736/cvl.v2i2.73.
R. Randa and A. Mahyudin, “Pengaruh Persentase Serat Pelepah Pisang Terhadap Sifat Fisik dan Mekanik Papan Semen-Foam agent,†J. Fis. Unand, vol. 8, no. 1, pp. 46–51, 2019, doi: 10.25077/jfu.8.1.46-51.2019.
I. Purnawan and A. Prabowo, “Pengaruh Penambahan Limestone terhadap Kuat Tekan Semen Portland Komposit,†J. Rekayasa Proses, vol. 11, no. 2, p. 86, 2018, doi: 10.22146/jrekpros.31136.
S. W. I. Pratama, N. Rauf, E. Juarlin, S. W. I. Pratama, N. Rauf, and E. Juarlin, “Pembuatan dan Pengujian Kualitas Semen Portland Yang Diperkaya Silikat Abu Ampas Tebu ( Fabrication and Quality Test of Cement Portland With Enriched by Silicate Sugarcane Bagasse Ash ),†J. Fis. FMIPA Unhas, 2014.
Susilowati, “Pemanfaatan Serbuk Marmer Sebagai Bahan Alternatif Pengganti Semen Pada Campuran Beton Normal,†J. Arsit., vol. 1, no. 2, pp. 16–24, 2011.
K. Amna, Wesli, and Hamzani, “Pengaruh Penambahan Serat Tandan Sawit Terhadap Kuat Tekan Dan Kuat Lentur Beton,†J. Din., vol. 4, no. 2, pp. 11–20, 2014.
I. M. Salain, “Pengaruh jenis semen dan jenis agregat kasar terhadap kuat tekan beton,†Teknol. dan Kejuru., vol. 32, no. 1, pp. 63–71, 2009.
A. I. Candra, E. Gardjito, Y. Cahyo, and G. A. Prasetyo, “Pemanfaatan Limbah Puntung Rokok Filter Sebagai Bahan Campuran Beton Ringan Berpori,†UKaRsT, vol. 3, no. 1, p. 82, 2019, doi: 10.30737/ukarst.v3i1.365.
E. Gardjito, A. I. Candra, and Y. Cahyo, “Pengaruh Penambahan Batu Karang Sebagai Substitusi Agregat Halus Dalam Pembuatan Paving Block,†UKaRsT, vol. 2, no. 1, pp. 38–46, 2018.
A. Gunawan and Elhusna, “PERBAIKAN PERILAKU KUAT TEKAN BETON AIR RAWA DENGAN METODE PENYARINGAN AIR,†Inersia, vol. 6, no. 1, pp. 73–80, 2014.
H. Pratikto, “Penelitian Kuat Uji Tekan Beton Dengan Memanfaatkan Limbah Beton Yang Tidak Terpakai,†UKaRsT, vol. 1, no. 2, p. 21, 2017, doi: 10.30737/ukarst.v1i2.411.
S. Winarto, “Pemanfaatan Serat Ijuk Sebagai Material Campuran Dalam Beton Untuk Meningkatkan Kemampuan Beton Menahan Beban Tekan Studi Kasus: Pembangunan Homestay Singonegaran Kediri,†UKaRsT, vol. 1, no. 1, pp. 1–10, 2017.
Downloads
Published
Issue
Section
License
Authors who publish with this journal agree to the following terms:
(1) The copyright of published articles will be transferred to the journal as the publisher of the manuscript. Therefore, the author needs to confirm that the copyright has been managed by the publisher with the Publication Right Form which must be attached when submitting the article.
(2) Publisher of JURMATEKS is Kadiri University.
(3) The copyright follows Creative Commons Attribution-ShareAlike License (CC BY SA): This license allows to Share copy and redistribute the material in any medium or format, Adapt remix, transform, and build upon the material, for any purpose, even commercially.